|Ahead of print publication
Effect of sterilization on cyclic fatigue resistance of Proflexendo endodontic rotary files
Emad O Alshwaimi
Department of Restorative Dental Sciences, College of Dentistry, Imam Abdulrahman Bin Faisal University, Dammam, Saudi Arabia
Emad O Alshwaimi,
Department of Restorative Dental Sciences, College of Dentistry, Imam Abdulrahman Bin Faisal University, P. O. Box 1982, Dammam 31441
Source of Support: None, Conflict of Interest: None
Background: Proflexendo file (Nexen, Houston, TX, USA) is a recently developed, novel nickel-titanium rotary file. However, several physical properties of the Proflexendo system remain to be investigated.
Objectives: The aim of this study was to determine the effect of sterilization on cyclic resistance of Proflexendo files.
Material and Methods: A total of 120 unused Proflexendo rotary files (40 each of file sizes 40/0.04, 30/0.04 and 20/0.06) were used in this study. Each set of files was subdivided into four groups of ten files. Group 1 did not undergo any sterilization (control), Group 2 underwent two rounds (2×) of sterilization, Group 3 five rounds (5×) and Group 4 ten rounds (10×). Cyclic fatigue resistance was tested using an artificial canal with a 5-mm radius curve.
Results: The nonsterilized size 30/0.04 files had the highest cycles to failure, followed by the nonsterilized size 40/0.04 and 20/0.06 files (P < 0.001). With increasing rounds of sterilization, cycles to failure reduced for sizes 40 (2×, 5× and 10×) and 30 (2×) files compared with nonsterilized sizes 40 (P < 0.05) and 30 files (P < 0.001), respectively.
Conclusion: Under the conditions of the current study, the results provide preliminary evidence that autoclave sterilization of Proflexendo rotary files reduced their cyclic fatigue resistance, except for size 20 (2× and 5×) and 30 (10×) files, in which resistance increased. Single use of this file is recommended to reduce the risk of separation.
Keywords: Cyclic fatigue, endodontic rotary file, nickel-titanium, Proflexendo, sterilization
|How to cite this URL:|
Alshwaimi EO. Effect of sterilization on cyclic fatigue resistance of Proflexendo endodontic rotary files. Saudi J Med Med Sci [Epub ahead of print] [cited 2019 May 19]. Available from: http://www.sjmms.net/preprintarticle.asp?id=251924
| Introduction|| |
Since the introduction of the first nickel-titanium rotary files (NTRF) to overcome the rigidity of stainless steel files, several types of NTRFs have become commercially available. The flexibility of NTRF allows these instruments to produce more centered preparations.,,, An adequate understanding of the physical properties and limitations of endodontic files can reduce undesirable procedural accidents, such as separation of the file in the canal, transportation and strip perforation. Previous reports have shown that cyclic fatigue resistance plays a major role in the separation of rotary files in canals with curvatures., This is due to cycles of tension and compression that occur when a file is freely rotating in curved canals. At a certain point, the file reaches its flexural limit and fractures.,
Infection control and cross-infections are major concerns for both patients and health-care providers, and thus endodontic instruments and files should always be sterilized to prevent the transmission of contagious diseases. Several studies have investigated the effects of sterilization on the physical properties of NTRF, with contrasting results. Some investigators concluded that sterilization negatively affects the physical properties of NTRF and causes files to prematurely fail.,,,, Other investigators have reported that up to ten cycles of heat sterilization do not increase the chance of NTRF failure.,
Recently, a novel nickel-titanium rotary file, the Proflexendo file (Nexen, Houston, TX, USA), was developed. This file is manufactured with controlled memory nickel-titanium technology and a triangular cross-section. Several recent studies have shown that files made from controlled memory technology have superior physical properties compared with rotary file made using other manufacturing techniques.,,, According to the manufacturer's instructions, to achieve a working length, the Proflexendo system should be used in a crown-down movement, starting with size 40/0.04 file, followed by size 30/0.04 and then size 20/0.06 files. Compared with the Profile Vortex size 30/0.04 file, the Proflexendo size 30/0.04 file has been found to have a significantly higher number of cycles to failure (CTF). However, several physical properties of the Proflexendo system remain to be investigated. Therefore, the aim of this study was to evaluate the cyclic fatigue properties of three sizes of Proflexendo file with and without sterilization. The null hypothesis is that there is no difference between the cyclic fatigue resistance of different sizes of Proflexendo files, and that sterilization has no effect on their fatigue resistance.
| Materials and Methods|| |
Files and sterilization
A total of 120 unused Proflexendo files (Nexden, Houston, TX, USA) of the following sizes were used for comparison: 40/0.04 (n = 40), 30/0.04 (n = 40) and 20/0.06 (n = 40) files (all 25 mm). Each set of files was subdivided into four groups of 10 files. The control group (Group 1) did not undergo any sterilization, whereas the other files were subjected to two rounds (2×) (Group 2), five rounds (5×) (Group 3) or ten rounds (10×) (Group 4) of sterilization. For each round of sterilization, the instruments were subjected to an autoclave cycle at a temperature of 134°C for 25 min, followed by 15 min of drying.
Cyclic fatigue testing
After completion of the respective number of autoclave cycles, all files (including those in Group 1) were subjected to fatigue testing, as previously described. Briefly, a stationary stainless steel frame covered with a mobile transparent acrylic piece was fixed with screws to a steel block [Figure 1]. An artificial canal was machined within the steel block to achieve a 5-mm radius curve, a curvature of 60° and a groove of 1 mm, according to the recommendations of Pruett et al. To ensure a reproducible three-dimensional relationship to the artificial canal in the steel block, an electric rotary hand-piece was fixed to the main frame. Each rotatory file was mounted in the hand-piece and precisely positioned to the same point in the testing block. Lubrication oil (WD-40 Company, San Diego, CA, USA) was used to reduce frictional heat.
|Figure 1: Cyclic fatigue testing machine and enlargement of the file within the groove (α – Angle of curvature; r – radius of curvature)|
Click here to view
All files were rotated at a fixed speed of 500 rpm (according to the manufacturer's instructions) in a 6:1 reduction hand-piece (Sirona, Bensheim, Germany) powered by a torque-controlled endodontic motor (Silver; VDW, Munich, Germany). To maintain consistency, the same operator performed the entire cyclic fatigue testing. Time to separation for each instrument was recorded using a digital 1/100 s chronometer. The total number of CTF for each instrument was calculated by multiplying the time to fracture by the number of rotations/min. Each separated segment of each file was measured with a digital caliper (Mitutoyo, Tokyo, Japan).
Data were analyzed using SPSS (v20.0; IBM, Chicago, IL, USA). Total CTF is presented as mean ± standard deviation (SD) values. Analysis of variance was applied to compare the mean cyclic failure and length of separated fragment among the three file sizes tested and the four sterilization conditions by splitting the datasheet with respect to sterilization techniques and file sizes, respectively. Post hoc Tukey's test was used to compare the means. P ≤ 0.05 was considered statistically significant.
| Results|| |
Nonsterilized Proflexendo files size 30/0.04 had the highest CTF followed by file sizes 40/0.04 and 20/0.06 (P < 0.001) [Table 1]. After sterilization, size 40/0.04 files (2×, 5× and 10×) had significantly lower CTF compared with nonsterilized size 40/0.04 files (P < 0.05). While 2× and 5× sterilized size 30/0.04 files had lower CTF compared with control (P < 0.001 and P > 0.05; respectively), the CTF of 10× sterilized size 30/0.04 files increased compared with control (P < 0.05). In contrast, the CTF of 2× and 5× sterilized size 20/0.06 file was higher than that of the control (P < 0.001), while the CTF of 10× sterilized size 20/0.06 file was lower than that of the control (P > 0.001). There were no significant differences in the mean fragment length of the three file sizes (P > 0.05) [Table 2].
|Table 1: Mean (±SD) number of cycles to failure for each file size according to sterilization condition|
Click here to view
| Discussion|| |
Prolonged and repeated clinical usage of endodontic files has been found to negatively affect the physical properties of some rotary files, which in turn can lead to file failure. Fear that a rotary instrument will undergo separation is one of the most common reasons clinicians avoid using NTRFs.,, Previously, some reports attributed the majority of rotary file failures to cyclic fatigue., Because files are often reused multiple times, they undergo repeated rounds of sterilization. Although the single use of files is advocated, it is rarely practiced. For example, in a survey of dentists in Germany, only 5% of the respondents reported using endodontic files as single-use files. Some studies have concluded that single use of endodontic files is not justified, while other studies have described the use of a modified cleaning protocol for endodontic files to accommodate their reuse.
To the best of the author's knowledge, this is the first study to test and compare the cyclic fatigue resistance of all three Proflexendo file sizes with and without increasing rounds of sterilization. Rotary file systems usually comprise different files with varying tapers and tip sizes, which may affect their resistance to fracture. Proflexendo files are manufactured using a controlled memory nickel–titanium technology, which involves a novel thermomechanical process that controls the memory of the file; this innovation allows the file to exhibit superior flexible properties.,,,, The current study found that the cyclic fatigue resistance of nonsterilized size 30/0.04 Proflexendo files was approximately 296% and 220% greater than that of sizes 20/0.06 and 40/0.04 files, respectively. Because size 40 file has a larger tip size and 20 has a larger taper than size 30 file, there is an increased tendency to revert to its original shape. This, in turn, could create higher stresses when rotating in the inner side of the curve and lead to an earlier cyclic failure, thereby explaining the difference observed in this study. Further, the larger size and taper of these files can result in more heat being generated during the cyclic fatigue test and friction of the metal with walls of the artificial canal, leading to some changes in the metallurgic structure of the files.
An earlier study demonstrated that Proflexendo size 30/0.04 file has almost 500% higher resistance to cyclic fatigue than Profile Vortex 30/0.04 file. When taken together with the results of the current study, this indicates that Proflexendo size 30/0.04 file is not only most appropriate for use compared with other brands but also among other sizes of Proflexendo files.
Using the autoclaving cycles described in previous studies,,, this study found a significant reduction in the CTF of almost all sterilized files (2×, 5× and 10× cycles) compared with nonsterilized files. However, 10× size 30/0.04 and 2×, 5× size 20/0.06 sterilized files had a higher resistance to cyclic fatigue compared with the controls – there is no plausible explanation for this increase in CTF. The higher SD in these groups compared with other groups may be indicative of manufacturing differences between files from the same group; however, further studies are required to test this hypothesis.
The results of this study are in agreement with the findings of Casper et al., who evaluated the effect of autoclave sterilization on torsional resistance of three different manufacturing techniques of rotary files, including controlled memory files, and found significant discrepancies in the files' behavior. The current study results are also in agreement with that of Zhao et al., who evaluated the effect of sterilization on Hyflex size 30/0.06 file made from controlled memory alloy and found that 10 cycles of sterilization increased its cyclic fatigue resistance compared with nonsterilized Hyflex size 30/0.06 file.
In contrast to the findings of the current study, a previous study found that repeated autoclaving cycles did not have a notable effect on the CTF of size 40 rotary files, except in K3 XF files, which had a higher CTF after sterilization compared with the control. The results of the current study are also in disagreement with that of Canalda-Sahli et al., who indicated that sterilization did not significantly affect the flexibility, cutting efficiency or resistance to cyclic and torsional fatigue in the K-files of all sizes ranging from 25 to 40, and with that of Hilfer et al., who indicated that sterilization did not significantly affect the GT series X size 20/0.06 files. Similarly, the fracture of ProFile rotary files (Dentsply Maillefer, Ballaigues, Switzerland) did not increase after 10 cycles of heat sterilization, whereas exposure of ProFile rotary files to dry heat and autoclave sterilization did increase their resistance to cyclic fatigue.
Based on the results of the present study, which indicated differences in the cyclic fatigue resistance between the three files tested and a significant effect of sterilization, we reject the proposed null hypothesis.
| Conclusion|| |
Under the conditions of the current study, the results provide preliminary evidence that autoclave sterilization reduced the cyclic fatigue resistance of Proflexendo files, except in 2× and 5× 20 and 10× 30 files, where the resistance increased. Single use of this file may be recommended to reduce the risk of separation, especially with sizes 40 and 20. Further studies should evaluate the observed differences in the cyclic behavior between different sizes of Proflexendo file and its effect in clinical usage and compare them with other commercially available rotary files.
The author would like to thank Nexen Company for providing Proflexendo files, Mr. Lindsey Mateo for laboratory assistance and Mr. Intisar Siddiqui for help with statistical techniques.
Financial support and sponsorship
Conflicts of interest
There are no conflicts of interest.
| References|| |
Walia HM, Brantley WA, Gerstein H. An initial investigation of the bending and torsional properties of nitinol root canal files. J Endod 1988;14:346-51.
Esposito PT, Cunningham CJ. A comparison of canal preparation with nickel-titanium and stainless steel instruments. J Endod 1995;21:173-6.
Gergi R, Rjeily JA, Sader J, Naaman A. Comparison of canal transportation and centering ability of twisted files, pathfile-Protaper system, and stainless steel hand K-files by using computed tomography. J Endod 2010;36:904-7.
Short JA, Morgan LA, Baumgartner JC. A comparison of canal centering ability of four instrumentation techniques. J Endod 1997;23:503-7.
Kosa DA, Marshall G, Baumgartner JC. An analysis of canal centering using mechanical instrumentation techniques. J Endod 1999;25:441-5.
Lopes HP, Gambarra-Soares T, Elias CN, Siqueira JF Jr., Inojosa IF, Lopes WS, et al.
Comparison of the mechanical properties of rotary instruments made of conventional nickel-titanium wire, M-wire, or nickel-titanium alloy in R-phase. J Endod 2013;39:516-20.
Goo HJ, Kwak SW, Ha JH, Pedullà E, Kim HC. Mechanical properties of various heat-treated nickel-titanium rotary instruments. J Endod 2017;43:1872-7.
Zelada G, Varela P, Martín B, Bahíllo JG, Magán F, Ahn S. The effect of rotational speed and the curvature of root canals on the breakage of rotary endodontic instruments. J Endod 2002;28:540-2.
Lopes HP, Ferreira AA, Elias CN, Moreira EJ, de Oliveira JC, Siqueira JF Jr. Influence of rotational speed on the cyclic fatigue of rotary nickel-titanium endodontic instruments. J Endod 2009;35:1013-6.
Communicable Diseases Network of Australia. Infection Control Guidelines for the Prevention of Transmission of Infectious Diseases in the Health Care Setting. Canberra: Communicable Diseases Network of Australia, Commonwealth of Australia; 2004.
Eggert C, Peters O, Barbakow F. Wear of nickel-titanium lightspeed instruments evaluated by scanning electron microscopy. J Endod 1999;25:494-7.
Rapisarda E, Bonaccorso A, Tripi TR, Condorelli GG, Torrisi L. Wear of nickel-titanium endodontic instruments evaluated by scanning electron microscopy: Effect of ion implantation. J Endod 2001;27:588-92.
Schäfer E. Effect of sterilization on the cutting efficiency of PVD-coated nickel-titanium endodontic instruments. Int Endod J 2002;35:867-72.
Alapati SB, Brantley WA, Svec TA, Powers JM, Nusstein JM, Daehn GS. SEM observations of nickel-titanium rotary endodontic instruments that fractured during clinical use. J Endod 2005;31:40-3.
Valois CR, Silva LP, Azevedo RB. Multiple autoclave cycles affect the surface of rotary nickel-titanium files: An atomic force microscopy study. J Endod 2008;34:859-62.
Silvaggio J, Hicks ML. Effect of heat sterilization on the torsional properties of rotary nickel-titanium endodontic files. J Endod 1997;23:731-4.
Khabiri M, Ebrahimi M, Saei MR. The effect of autoclave sterilization on resistance to cyclic fatigue of hero endodontic file #642 (6%) at two artificial curvature. J Dent (Shiraz) 2017;18:277-81.
Topçuoǧlu HS, Topçuoǧlu G, Akti A, Düzgün S.In vitro
comparison of cyclic fatigue resistance of Protaper next, Hyflex CM, Oneshape, and Protaper universal instruments in a canal with a double curvature. J Endod 2016;42:969-71.
Kaval ME, Capar ID, Ertas H. Evaluation of the cyclic fatigue and torsional resistance of novel nickel-titanium rotary files with various alloy properties. J Endod 2016;42:1840-3.
Capar ID, Ertas H, Arslan H. Comparison of cyclic fatigue resistance of novel nickel-titanium rotary instruments. Aust Endod J 2015;41:24-8.
AlShwaimi E. Cyclic fatigue resistance of a novel rotary file manufactured using controlled memory Ni-Ti technology compared to a file made from M-wire file. Int Endod J 2018;51:112-7.
Gambarini G. Cyclic fatigue of profile rotary instruments after prolonged clinical use. Int Endod J 2001;34:386-9.
Parashos P, Gordon I, Messer HH. Factors influencing defects of rotary nickel-titanium endodontic instruments after clinical use. J Endod 2004;30:722-5.
Alshwaimi E. The uptake of nickel-titanium rotary files in Saudi Arabia. Int J Dent 2012;2012:484291.
Shen SM, Deng M, Wang PP, Chen XM, Zheng LW, Li HL, et al.
Deformation and fracture of K3 rotary nickel-titanium endodontic instruments after clinical use. Int Endod J 2016;49:1088-94.
Elnaghy AM, Elsaka SE. Mechanical properties of Protaper Gold nickel-titanium rotary instruments. Int Endod J 2016;49:1073-8.
Sonntag D, Martin E, Raab WH. Representative survey on the reprocessing of endodontic instruments in Germany. Br Dent J 2016;220:465-9.
Parashos P, Linsuwanont P, Messer HH. A cleaning protocol for rotary nickel-titanium endodontic instruments. Aust Dent J 2004;49:20-7.
Zhou HM, Shen Y, Zheng W, Li L, Zheng YF, Haapasalo M. Mechanical properties of controlled memory and superelastic nickel-titanium wires used in the manufacture of rotary endodontic instruments. J Endod 2012;38:1535-40.
King JB, Roberts HW, Bergeron BE, Mayerchak MJ. The effect of autoclaving on torsional moment of two nickel-titanium endodontic files. Int Endod J 2012;45:156-61.
Casper RB, Roberts HW, Roberts MD, Himel VT, Bergeron BE. Comparison of autoclaving effects on torsional deformation and fracture resistance of three innovative endodontic file systems. J Endod 2011;37:1572-5.
Li XF, Zheng P, Xu L, Su Q. The influence of autoclave sterilization on surface characteristics and cyclic fatigue resistance of 3 nickel-titanium rotary instruments. Shanghai Kou Qiang Yi Xue 2015;24:690-5.
Zhao D, Shen Y, Peng B, Haapasalo M. Effect of autoclave sterilization on the cyclic fatigue resistance of thermally treated nickel-titanium instruments. Int Endod J 2016;49:990-5.
Plotino G, Costanzo A, Grande NM, Petrovic R, Testarelli L, Gambarini G, et al.
Experimental evaluation on the influence of autoclave sterilization on the cyclic fatigue of new nickel-titanium rotary instruments. J Endod 2012;38:222-5.
Canalda-Sahli C, Brau-Aguadé E, Sentís-Vilalta J. The effect of sterilization on bending and torsional properties of K-files manufactured with different metallic alloys. Int Endod J 1998;31:48-52.
Hilfer PB, Bergeron BE, Mayerchak MJ, Roberts HW, Jeansonne BG. Multiple autoclave cycle effects on cyclic fatigue of nickel-titanium rotary files produced by new manufacturing methods. J Endod 2011;37:72-4.
Viana AC, Gonzalez BM, Buono VT, Bahia MG. Influence of sterilization on mechanical properties and fatigue resistance of nickel-titanium rotary endodontic instruments. Int Endod J 2006;39:709-15.
[Table 1], [Table 2]